고온 초전도체 Y_1-x Nd_x Ba₂Cu₃O_7-y의 특성과 Raman Scattering에 관한 연구

Title
고온 초전도체 Y_1-x Nd_x Ba₂Cu₃O_7-y의 특성과 Raman Scattering에 관한 연구
Other Titles
Study on the Characteristic and the Raman Scattering of High Temperature Superconductor Y_1-x Nd_x Ba₂Cu₃O_7-y
Authors
孫定沃
Issue Date
1993
Department/Major
교육대학원 과학교육전공물리교육분야
Keywords
고온 초전도체특성Raman ScatteringHigh Temperature Superconductor
Publisher
이화여자대학교 교육대학원
Degree
Master
Advisors
이종록
Abstract
The characteristic of high temperature superconductor Y_(1-x)Nd_(x)Ba_(2)Cu_(3)0_(7-y) ( x = 0.03, 0.07, 0.10 ) have been investigated. The measurement of magnetisation and resistivity show that superconducting transition temperature is about 90 K.XRD patterns show that crystal structures are orthorhombic. Raman active normal modes were predicted theorectically and measured at 506,440,340 cm^(-1). With increasing y, the stretching mode of 506 cm^(-1) peak correalted with Cu(1) - O(4) bond vibration shifts downward. Judging from the whole experimental data, the most important thing is that the determination of superconductivity of Y_(1)Ba_(2)Cu_(3)0_(7-y) system is oxygen contents in Cu - 0 plane.;고온 초전도체 Y_(1)Ba_(2)Cu_(3)O_(7-y) 계에서 yttrium 을 이온 반지름이 큰 neodymium으로 치환한 Y_(1-x)ND_(x)Ba_(2)Cu_(3)O_(7-y) ( x = 0.03, 0.07, 0.10 ) 의 여러 가지 물리적 특성들을 자화 ( magnetisation ) 와 비저항 ( resistivity ) 측정, 반자성 ( Meissner effect ) 과 SEM 관찰, 라만 산란 ( raman scattering )과 XRD 실험을 통해 알아 보았다. 자화와 비저항 측정으로 시료들의 초전도 전이 온도 Tc가 치환량이 증가할수록 감소하지만 90 K 근처임을 확인하였고, XRD 실험을 통해 cell 의 구조가 초전도성을 나타내는 사방정계 ( orthorhombic ) 구조라는 것이 확인되었다. 치환량의 증가에 따른 초전도성의 감소는 산소 농도 y 값의 변화, 치환 농도의 차이, polycrystal 인 grain 의 배열 상태가 다르기때문이라고 생각된다.
Fulltext
Show the fulltext
Appears in Collections:
교육대학원 > 물리교육전공 > Theses_Master
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE