Raman scattering studies of YBa2Cu3O7-X films grown by high-rate e-beam co-evaporation

Abstract

We present results of Raman scattering studies of superconducting YBa 2Cu3o7-x (YBCO) films grown by a high-rate electron-beam co-evaporation method. It is shown by X-ray diffraction that the as-grown YBCO films have a highly c-axis oriented and in-plane aligned texture. Raman scattering measurements were used to study optical phonon modes, oxygen content and second phases of the YBCO coated conductors. Raman spectra of YBCO films with lower-transport properties exhibit additional phonon modes at ∼ 300 cm-1, ∼ 600 cm-1, and ∼ 630 cm-1, which are related to second-phases such as Ba2Cu3O 5.9 and BaCuO2. We also performed micro-Raman scattering measurements, which enable the local characterization of the material over a few micrometer scales. We could clearly determine the chemical homogeneities of the films on which we could not have information using XRD. Our results strongly suggest that micro-Raman scattering can be a very effective tool for characterizing structural and chemical properties, which is essential for optimizing growth conditions. © 2007 IEEE.