폴리에스테르 필름의 그라프트 중합에 관한 연구

Abstract

Graft polymerization of acrylic acid (AA) and styrene on poly (ethylene terephthalate) (PET) film using benzoyl peroxide (BPO) as initiator was investigated under different conditions including monomer concentration, initiator concentration, polymerization temperature and time. The rate of grafting was evaluated varying the concentration of monomer, initiator, temperature and time. It was found that maximum percent grafting occurred when styrene/AA mixtures at a ratio of 80:20 was used. Increasing the ratio of styrene monomer in the styrene/AA mixture was accompanied by enhancement in percent grafting. It was studied that there is a synergistic phenomenon when styrene/AA mixtures are grafted to PET film. The results indicate that, in the styrene/AA mixture styrene exhibits negative synergism and AA exhibits positive synergism. Grafting of AA, styrene to PET film resulted in considerable improvement in moisture regain Moisture regain of PET film grafted with styrene is higher than that of AA. This is substantiated by the finding that increasing the mositure regain is mainly due to open internal structure.;BPO를 개시제로 하여 스티랜과 아크릴산을 폴리에스테르(PET)필름에 그라프트 중합을 시키면서 단량체의 농도, 개시제 농도, 반응 온도, 반응 시간 등의 제반조건이 그라프트 중합에 미치는 영향을 조사하였다. 또한 PET의 그라프트 중합에 스티렌/아크릴산 혼합 단량체가 사용될 때의 synergism 현상을 연구하였는데 스티렌/아크릴산의 비율이 상승할수록 그라프트율이 증가하여 스티렌/아크릴산= 80/20에서 최대의 그라프트율에 도달하였다. 각 단량체의 측면에서 보면 스티렌에서는 음의 synergism이 나타났으며 아크릴산에서는 양의 synergism이 나타났다. 스티렌이 그라프트 중합된 PET에서의 수분율이 아크릴산이 그라프트 중합된 PET에 비해서 높기 때문에 그라프트 중합에 의한 수분율 상승의 원인은 주로 PET분자 구조 내부에 도입된 열린 구조가 주원인으로 밝혀졌다.