H2O2-sensitive Degradable Thermogel

Abstract

An oxalate-connected thermogel of poly(ethylene glycol)-poly(propylene glycol)-poly(ethylene glycol) multiblock copolymers was prepared as a hydrogen peroxide (H2O2)-sensitive degradable polymer (HP-DP). As the temperature increased, a unimer-to-micelle transition accompanying the endothermic process was observed in UV-vis spectroscopy, dynamic light scattering, and microcalorimetry. HP-DP aqueous solutions underwent sol-gel-sol transitions in a concentration range of 8.0-28.0 wt.% as the temperature increased. The sol-to-gel transition of HP-DP aqueous solution (20.0 wt.%) occurring at about 15-25 ℃ accompanied 4.8-4.9 cal/g polymer and the transition was reversible. Unique degradation properties of the HP-DP thermogel were investigated by comparing mass loss, molecular weight, and drug release profiles at 0.0 and 0.1 mM of H2O2. The duration as a gel exhibited less than 7 days. Mass loss, degradation of polymer, and model drug (vitamin E) release from the in-situ formed gel was accelerated in the presence of H2O2. The oxalate connected thermogel can be promising as a H2O2-sensitive drug delivery system.;본 연구에서는 과산화수소-민감성 분해 가능한 써모젤링 고분자인 옥실레이트로 연결된 폴리(에틸렌 글리콜)-폴리(프로필렌 글리콜)-폴리(에틸렌 글리콜) (에이치피-디피) 다중블록 공중합체를 합성하였다. 이는 0.1 퍼센트 농도일 때, 온도가 증가함에 따라 자외선-가시광선 분광광도계, 동적 광 산란법, 미세 열량 분석기에서 흡열 과정이 동반된 유니머에서 미셀로의 전이가 관찰되었다. 또한 에이치피-디피 수용액은 온도가 증가함에 따라 8.0에서 28.0 퍼센트의 농도 범위에서 졸-젤-졸의 전이를 보였다. 한편 에이치-디피 써모젤의 독특한 분해 성질은 과산화수소 0 밀리 몰 농도와 0.1 밀리 몰 농도에서 질량 손실, 분자량, 약물 방출 개요를 비교하여 조사하였다. 과산화수소 0.1 밀리 몰 농도에서 젤의 지속기간은 7일 이하로 관찰되었다. 형성된 젤에서 질량 손실, 고분자의 분해, 모델 약물 (비타민 이) 방출은 과산화수소가 존재할 때 가속화되었다. 따라서 본 옥실레이트로 연결된 써모젤, 에이치피-디피는 과산화수소-민감성 약물 전달 시스템으로 적용될 수 있다.