dc.description.abstract | Using sol-gel processing and high temperature annealing, Au metal nanoclusters were prepared in TiO2 thin films. Au nanocrystal formation was confirmed by X-ray diffraction and its average particle size at the heat-treatment range of 500-900°C was measured as 16-29 nm in diameter by transmission electron microscopy. Compared with Au-SiO2, it has been observed that the peak of surface plasmon absorption is red-shifted to around 642 nm and its width is much broader, due to a strong interaction between the metal surface and the surrounding matrix. | - |
dc.language | English | - |
dc.publisher | Elsevier Science Ltd, Exeter, United Kingdom | - |
dc.title | Microstructure and surface plasmon absorption of sol-gel-prepared Au nanoclusters in TiO2 thin films | - |
dc.type | Article | - |
dc.relation.issue | 2 | - |
dc.relation.volume | 11 | - |
dc.relation.index | SCOPUS | - |
dc.relation.startpage | 195 | - |
dc.relation.lastpage | 201 | - |
dc.relation.journaltitle | Nanostructured Materials | - |
dc.identifier.doi | 10.1016/S0965-9773(99)00032-X | - |
dc.identifier.wosid | WOS:000081172200005 | - |
dc.identifier.scopusid | 2-s2.0-0032688366 | - |
dc.author.google | Lee M. | - |
dc.author.google | Chae L. | - |
dc.author.google | Lee K.C. | - |
dc.contributor.scopusid | 이민영(55582235800) | - |
dc.date.modifydate | 20190901081003 | - |