Raman Scattering Studies of YBCO Coated Conductors

Title
Raman Scattering Studies of YBCO Coated Conductors
Authors
이은영
Issue Date
2007
Department/Major
대학원 나노과학부
Publisher
이화여자대학교 대학원
Degree
Master
Abstract
We present results of Raman scattering studies of superconducting YBa2Cu3O7-δ (YBCO) films grown by electron beam co-evaportion, chemical vapor deposition and metal-organic deposition methods. It is shown by x-ray diffraction that all the asgrown YBCO films have a highly c-axis oriented and in-plane aligned texture. Raman scattering measurements were used to investigate optical phonon modes, oxygen contents, structural properties, and second phases of the YBCO coated conductors. Raman spectra of YBCO films with lower-transport qualities exhibit additional phonon modes at ~300 cm -1 , ~600 cm-1 and ~630 cm-1 , which are related to second-phases such as Ba 2Cu3O5.9 and BaCuO2 . Our results strongly suggest that Raman scattering be useful foroptimizing YBCO film growth conditions.;YBCO(YBa2Cu3O7-δ)는 고온 초전도체로 최근 산업화를 위한 연구들이 활발히 진행되고 있는 물질이다. 그 중에서도 YBCO coated conductor를 시간과 경제적 측면에서 보다 효율적으로 증착시키키 위한 연구들이 많이 이루어지고 있다. 본 연구에서는 Electron beam co-evaporation, CVD, TFA- MOD의 방법으로 증착시킨 YBCO coated conductors의 라만 산란 분광을 연구하였다. 라만 산란은 X선 회절(XRD) 실험으로는 알 수 없는 국소적인 분석이 가능하고 micro 라만 산란을 통해서는 YBCO coated conductors의 여러 곳을 측정함으로써 위치에 따른 분광학적 특성을 분석할 수 있다. 이는 주사전자현미경(SEM)으로 실험한 결과와 일치하였다. 따라서 라만 산란은 YBCO coated conductor의 최적의 증착 조건을 찾는데 유용한 도구가 될 것이다.
Fulltext
Show the fulltext
Appears in Collections:
일반대학원 > 화학·나노과학과 > Theses_Master
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE