YBa2-xGdxCU3O7-y 고온 초전도체의 물리적 특성

Abstract

The physical properties of high temperature superconductor YBa_(2-x)Gd_(x)Cu_(3)O_(7-y)(x=0, 0.03, 0.05, 0.07) have been investigated. Samples were analyzed by x-ray diffraction, resistivity, SEM(scanning electron microscope) photograph and Raman spectrum. The maximum critical temperature is 90K at x=0.03, the critical temperature Tc of the samples decreases with increasing Gd cocentration. The decrease of the critical temperature by Gd substitution in the crystal implies that the hole density in the crystal is the important parameter of the decision on the critical temperature Tc. And granular properties are the important parameters, too.;고온 초전도체 YBa_(2)Cu_(3)O_(7-y)에서 Ba의 일부를 Gd로 치환한 YBa_(2-x)Gd_(x)Cu_(3)O_(7-y) (x=0.03,0.05,0.07)시료들을 제작하고 SEM 관찰, X-선 회절 실험, 비저항 측정 실험, 자화율 측정 실험, Raman Spectrum 관찰등을 통해 이들 시료들의 물리적 특성을 알아 보았다. 초전도 임계온도 Tc 는 x=0.03 일때 90K, x=0.05 일때 88K, x=0.07 일때 89K였다. YBa_(2-x)Gd_(x)Cu_(3)O_(7-y) 의 임계온도는 시료의 결정구조 뿐 아니라 시료 내부의 grain 특성에도 많은 영향을 받음을 알 수 있었다.