Porcelain repair - Influence of different systems and surface treatments on resin bond strength
- Porcelain repair - Influence of different systems and surface treatments on resin bond strength
- Yoo, Ji-Young; Yoon, Hyung-In; Park, Ji-Man; Park, Eun-Jin
- Ewha Authors
- 박은진; 윤형인
- SCOPUS Author ID
- 박은진; 윤형인
- Issue Date
- Journal Title
- JOURNAL OF ADVANCED PROSTHODONTICS
- 2005-7806; 2005-7814
- vol. 7, no. 5, pp. 343 - 348
- Porcelain repair; Composite resin; Shear bond strength; Tribochemical silica coating
- KOREAN ACAD PROSTHODONTICS
- SCIE; SCOPUS; KCI
- PURPOSE. The purpose of this study was to evaluate the bond strength of composite resin on the fracture surface of metal-ceramic depending on the repair systems and surface roughening methods. MATERIALS AND METHODS. A total of 30 disk specimens were fabricated, 15 of each were made from feldspathic porcelain and nickel-chromium base metal alloy. Each substrate was divided into three groups according to the repair method: a) application of repair system I (Intraoral Repair Kit) with diamond bur roughening (Group DP and DM), b) application of repair system I with airborne-particle abrasion (Group SP and SM), and c) application of repair system II (CoJet Intraoral Repair System, Group CP and CM). All specimens were thermocycled, and the shear bond strength was measured. The data were analyzed using the Kruskal-Wall is analysis and the Mann-Whitney test with a significance level of 0.05. RESULTS. For the porcelain specimens, group SP showed the highest shear bond strength (25.85 +/- 3.51 MPa) and group DP and CP were not significantly different. In metal specimens, group CM showed superior values of bond strength (13.81 +/- 3.45 MPa) compared to groups DM or SM. CONCLUSION. Airborne-particle abrasion and application of repair system I can be recommended in the case of a fracture localized to the porcelain. If the fracture extends to metal surface, the repair system II is worthy of consideration.
- Appears in Collections:
- 의학전문대학원 > 의학과 > Journal papers
- Files in This Item:
There are no files associated with this item.
- RIS (EndNote)
- XLS (Excel)
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.