양모직물의 외관 및 태 변화를 위한 방축/축융가공의 동시적용 기초 연구

Title
양모직물의 외관 및 태 변화를 위한 방축/축융가공의 동시적용 기초 연구
Other Titles
A study of simultaneous shrink resist/felting treatment of wool gauze for the diversification of appearance and hand
Authors
정아현
Issue Date
2015
Department/Major
대학원 의류학과
Publisher
이화여자대학교 대학원
Degree
Master
Advisors
김종준
Abstract
With the recent changes into the information age, personality has been considered important and consumption levels have been advanced. The demand for the textiles of high quality and sensitivity for the consumers is increasing. Therefore, the values of the diverse, functional, and aesthetic clothing materials are considered important. To find such features of the clothing materials, physical and chemical characteristics of the textiles were understood and analyzed to improve the values of the products by changing emotional and physical features. Wool fabrics requires of different processing techniques not only for technical aspects but for emotional aspects. It is definitely positioned as a very important material in fashion industry. Shrink-resist treatment and shrink treatment of wool fabrics are to use utilize the variations caused by the properties of wool fabrics from different perspectives. In this study, the current commercially available Synthappret BAPs were selected to experiment by varying the applied amount of the processing agent. Under each condition, the wool fabrics were processed. Their shrink-resist effects were compared and physical features related to the shapes of the wool fabrics were compared. In addition, by shrink-processing the shrink-resist-treated wool fabrics and untreated processed fabrics, their effects resulted were compared. In each condition were compared to compare the dike effect the physical properties associated with the state of the wool fabric. To compare the effect of the addition of the dike milling processing textiles and raw textile processing by the milling process for processing raw wool fabrics and fabric processing ouster. 1. As a result of measuring the rate of contraction of wool fabrics specimens, the area contraction rate of CtrlF which was processed for shrinking without shrink-resist treatment agent has shrunk sharply into 11%. The specimens which were tried to shrink after the shrink-resist treatment had 2.9 to 4.5% area shrink rate. Their shrink was controlled in proportion to wet pick up amount. 2. In order to review the variation of basic features of each specimen, weight, thickness, density per unit area, air permeability, flex firmness were reviewed. As a result, the specimens which were tried to shrink after Synthappret BAPs treatment, contraction was controlled to be lower than that of untreated specimen. In the result of flex firmness, shrink-resist-treated specimens such as S110, S130, and S150 became remarkably stiff than Ctrl specimen. It means the shapes of the textiles became stiffen. On the other hand, in case of the specimens such as S110F, S130F, and S150F, when shrunk after processing shrink-resist treatment, processing agent among textiles are dropped out partially and divided to be smooth. 3. In the findings of the traits of KES, S150 specimen processed with shrink-resist treatment agent was found that it had a great resistance for sear strain. In addition, for specimens such as S110F, S130F, and S150F, restoration from shear strain seemed moderate since the attachment among cloths in the course of shrink-resist treatment was divided and the coating on the surface of each cloth remained. In this study, in order to realize cubic contrast effect by the appropriate combination of shrink-resist treatment and shrink treatment, quantitative and scientific conditions were found. To these ends, physical features and appearance of wool fabrics were analyzed. From such characteristics, cubic effect was adjusted precisely. Basic data to design texture could be secured. By using such basic data, it was judged that cubic contrast effect of wool fabrics with shrink-resist treatment and shrink treatment or physical traits variation could be predicted quantitatively.;최근 지식정보화시대로 변화되면서 개성이 중시되고 소비수준이 고급화되고 있다. 또한 소비자의 감성을 충족시킬 수 있는 고품질의 고감성 텍스타일에 대한 수요가 증대되고 있다. 이에 따라 의류소재의 다양성 및 기능적 ․ 심미적 차원의 가치가 중요하게 부각되고 있다. 이를 충족시키기 위해서 섬유가 지닌 물리적 ․ 화학적 특성을 이해하고 분석하여 감성과 물성을 변화시킴으로써 제품의 가치를 높일 수 있다. 양모직물은 의류용 소재로서 감성적인 측면뿐만 아니라 기술적인 측면에서 다양한 가공기술이 요구되어 패션산업에서 매우 중요한 위치를 차지하고 있다. 양모직물의 방축가공과 축융가공은 양모섬유의 특성으로 인해 발생하는 변화를 서로 다른 관점에서 활용하는 것이라고 할 수 있다. 본 연구에서는 현재 시판되는 방축가공제(Synthappret BAP)를 선정하여 그 가공제의 적용양을 변화시켜 실험하였다. 각 조건에서 양모직물을 처리하여 방축효과를 비교해 보고 양모직물의 태와 관련되는 물리적 성질을 비교하였다. 또한 방축가공한 양모직물과 미처리가공 직물에 대해 축융처리를 함으로써 방축가공 직물과 미처리가공 직물의 축융에 의한 효과를 비교하고자 하였다. 본 연구에서는 대조 시료군을 세분화하여 비교하였다. 1. 양모직물 시료의 수축률을 측정한 결과, 방축가공제를 처리하지 않고 축융을 진행한 시료(CtrlF)는 면적수축률이 11%로 급격히 수축하였다. 방축가공제를 처리하고 축융을 진행한 시료들은 면적수축률이(2.9~4.5%)로 wet pick up 양에 비례하여 수축이 억제된 경향이 보인다. 2. 각 시료의 기본 물리적 특성 변화를 살펴보기 위하여 단위면적당 중량, 두께, 밀도, 공기투과도, 플렉스 강연도를 살펴본 결과, 방축가공제를 미처리하고 축융을 진행한 시료는 단위면적당 중량과 두께가 현저히 증가하였다. 반면, 방축가공제를 처리하고 축융한 시료의 경우에는 수축의 억제되어 미처리 시료보다 낮아짐을 확인하였다. 플렉스 강연도의 결과에서는 방축가공제를 처리한 S110, S130, S150 시료는 Ctrl시료보다 모두 현저히 빳빳해졌다. 이는 직물의 태가 대체로 강경해진 것을 보여준다. 반면, S110F, S130F, S150F 시료들의 경우 방축가공제 처리 후 축융을 하면 섬유와 섬유 사이에 접착된 가공제가 일부탈락하고 분리되어 부드러워진 것을 알 수 있다. 3. KES 전단특성의 결과에서는 방축가공제를 처리한 S150시료는 전단 변형에 대한 저항이 큰 것을 알 수 있다. 또한 시료 S110F, S130F, S150F 는 방축가공 후의 축융과정에서 실과 실 사이의 접착은 분리되고, 각 실 표면의 코팅은 남게 되어 비교적 매끄러운 상태를 유지하게 되므로 전단변형에 대한 회복이 양호하게 된 것으로 보인다. 본 연구에서는 방축과 축융가공의 적절한 조합으로 입체적 대비 효과를 내기 위해 정량적이고 과학적인 조건들을 찾아보고자 하였다. 이러한 양모 직물의 물리적 성질과 외관특성을 분석하였다. 이러한 결과들로 인하여 정밀하게 입체효과를 조절하고 원하는 질감을 설계할 수 있는 기본적 데이터를 확보할 수 있었다. 또한 이들 기초데이터를 바탕으로 양모직물에 대해 방축가공/축융가공을 동시에 적용하여 입체적으로 차별화된 효과를 살펴보았다. 향후 방축/축융가공을 동시에 정밀하게 적용함으로써 보다 부가가치가 높은 소재의 개발 및 전개가 가능할 것으로 기대한다.
Fulltext
Show the fulltext
Appears in Collections:
일반대학원 > 의류학과 > Theses_Master
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE