The effect of post surface treatments on adhesion of a resin based luting agent to a fiber post

Title
The effect of post surface treatments on adhesion of a resin based luting agent to a fiber post
Other Titles
포스트 표면 처리가 레진 시멘트와 화이버 포스트의 접착력에 미치는 영향
Authors
최윤정
Issue Date
2008
Department/Major
임상치의학대학원 임상치의학과보철수복치의학전공
Publisher
이화여자대학교 임상치의학대학원
Degree
Master
Abstract
Purpose. The purpose of this in vitro study is to evaluate the influence of different post surface treatments on the bond strength of a luting agent to a fiber post. Material and methods. Radiopaque translucent fiber posts (D.T. Light-Post??, Bisco Inc., Schaumburg, IL, USA) and dual-curing resin based luting material (Variolink?? Ⅱ, Ivoclar Vivadent, Liechtenstein) were used in this study. Sixty eight fiber posts were divided into 4 groups and performed one of the following surface treatments procedures: no treatment group (control); silanization group (Monobond-S, Ivoclar Vivadent, Liechtenstein); airborne-particle abrasion group (Airsonic Aluminum oxide, Hagerwerken, Germany); or silanization subsequent to airborne-particle abrasion group. Specimens were bonded with dual-curing resin based luting agent on the post surface and stored in water at 37 ℃ for 24 hours. Shear bond strength (MPa) of the luting agent to the post was measured with universal testing machine with a crosshead speed of 1 mm/min. The data were statistically analyzed by ANOVA and the multiple comparisons Scheffe and Bonferrni test at the significance level of p=0.05. Results. The mean shear bond strength and standard deviations (MPa) were as follows: 25.92 ± 7.80 for no treatment group, 34.26 ± 7.80 for silanization group, 51.48 ± 13.31 for airborne-particle abrasion group, and 39.80 ± 13.44 for silanization subsequent to airborne-particle abrasion group. Shear bond strength of the luting agent to the post was significantly affected by surface treatments except silanization (p<.05). Treating the post’s surface with airborne-particle abrasion caused significantly higher bond strength compared with other treatments and silanization showed no significant effect. Conclusion. Within the limitation of this study, it can be concluded that the bond strength of resin luting agent to the fiber post was influenced by post surface treatments. Airborne-particle abrasion procedure may give a significant increase in bond strength between the post and the luting agent without additional treatments and this can simplify the clinical procedure.;이 논문의 목적은 포스트의 다양한 표면 처리가 레진 시멘트와 화이버 포스트의 결합 강도에 미치는 영향을 평가하는 것이다. 방사선 불투과성 반투명 화이버 포스트 (D.T. Light-Post??, Bisco, USA)와 dual-curing 레진 시멘트 (Variolink?? Ⅱ, Ivoclar Vivadent, Liechtenstein)를 실험에 사용하였다. 68개의 화이버 포스트를 다음과 같은 표면처리에 따라 4개의 실험군으로 나누었다: 무처리군 (대조군); 실란 처리군 (Monobond-S, Ivoclar Vivadent, Liechtenstein); 알루미나 분사 처리군 (Airsonic Aluminum oxide, Hagerwerken, Germany); 알루미나 분사 및 실란 혼합 처리군. 각각의 표면 처리 후에 시편들은 dual-curing 레진 시멘트를 이용하여 제조사의 지시대로 접착된 후, 37 ℃ 항온 수조에서 24시간 동안 보관되었다. 포스트와 레진 시멘트간 접착 계면의 전단결합강도는 만능시험기를 이용하여 crosshead speed 1 mm/min로 측정하였다. 측정 결과는 일원 배치 분산 분석 (ANOVA)과 다중 비교 Scheffe, Bonferroni 검정을 이용하여 유의수준 p<0.05로 통계 분석하였다. 실험 결과 화이버 포스트와 레진 시멘트 간의 전단결합강도는 포스트 표면 처리에 영향을 받았다. 알루미나 분사 처리한 포스트 군에서 다른 처리군들과 비교했을 때 가장 높은 전단결합강도가 측정되었다. 반면, 실란 단독 처리는 포스트의 접착 강도에 유의한 영향을 미치지 않았으며, 알루미나 분사 처리와 병행되었을 때 단독 알루미나 분사 처리만 한 것에 비해 오히려 접착강도의 감소를 보였다. 레진 화이버 포스트는 심미적이고 상아질과 유사한 탄성계수를 가져 치근 파절을 줄일 수 있기 때문에 근관 치료된 치아의 수복에서 광범위하게 사용되고 있다. 화이버 포스트와 레진 시멘트와의 접착결합강도는 포스트의 표면 처리에 영향을 받으며, 결론적으로 resin-based luting agent를 사용하여 fiber-reinforced epoxy resin post 접착 시 별도의 부가적인 술식 없이 알루미나 분사 처리만으로도 접착력의 향상을 기대할 수 있으며, 이는 임상 술식을 간소화하는 데 기여할 것으로 사료된다.
Fulltext
Show the fulltext
Appears in Collections:
임상치의학대학원 > 임상치주보철학전공 > Theses_Master
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE