화장토에 관한 연구

Title
화장토에 관한 연구
Authors
진숙현
Issue Date
1979
Department/Major
대학원 응용미술학과
Publisher
이화여자대학교 대학원
Degree
Master
Abstract
While Engobe is used in Inlaying or coating in our country, vitreous slip is unfamiliar to us and we are unaccustomed to using this method. Vitreous slip, unlike glaze, has the advantage that the potter can sufficiently perform his proposed touch and naturally expose texture different form the glaze, has the adbvantage that the potter can sufficiently perform his proposed touch and naturally expose texture different from the glaze; therefore it is open to apply to work variously. The reporter utilized Engobe used widely in Inlaying or underslip technique in Korea, adding texture developed to basic body in 9 compounds of basic engobe to use color material on the glaze or the body. To the best result of them, the reporter added Flux; lead-containing frits, leadless frit and red lead (Pb304) in different proportions separately. And then, reporter compared their melting states to the firing result of electric kiln at 1250ºC and firing result of down draft rectangular kiln. As a result of the experiment, the conpound with a little added volume of Yeo-ju clay is found comparatively high in degree of white color. And it is found that the case with added lead is clearer in firing color and more adoptable in melting condition than the case with added frit; therefore it is noticeable that red lead affected in the better way than the frit in efpressing the color. Generally, the more amount of Flux is added, the more phenomena of blistering and pinhole ocurred. Especially the leadless frtt can cause the worst defects. And the more severe phenomenon was shown where the vitreous slip containing any kind of flux is applied thickly. In producing a work, the best resulting condition of them and add reduction firing at 1250ºC. As a result, both of the conditions whether melted according to adding amount or not stuck well the glaze; therefore it is said to show the probability of using overslip with vitreous slip, In this reporter's work, after biscuit firing 900ºC to the thing forming on the wheel using basic body, applying the copper glaze red-spot glaze, black glaze and opalescent glaze, and then vitreou srlip with mineral oxide added, applied on it. As a result of the above work, the reporter was able to express the more delicate touch and could also expect the possibility of the vitreous coating. When coloring body or white body is used the more variable decoration harmonizing with the texture of body only by decorating with vitreous slip of various colors on the surface of the biscuited body.;우리나라에서 상감이나 분장에 쓰이는 화장토외에 용화화장토(vitreous slip)는 생소한 것이며 사용방법에도 물론 익숙치 못하다. 熔化化粧土는 釉藥과는 달리 作家의 意圖한 touch를 그대로 살릴 수 있는 잇점이 있으며, 자연히 釉藥과는 다른 질감을 나타내므로 보다 다양하게 作品에 응용할 수 있는 餘地가 있는 것이다. 필자는 우리나라에서 象嵌手法이나 粉粧技法에 널리 使用된 化粧土를 이용하여 融劑를 添加시킴으로써 熔化化粧土로 發展시켜 유약위에나 素地위에서 彩料로 응용해 보고자 한다. 먼저 9가지 化粧土의 調合物을 基本素地에 適用시켜 그中에서 좋은 結果를 보인 것에 有鉛 frit, 無鉛 frit, 光明丹을 각기 다른 비율로 添加시켜 그들의 熔融狀態를 1250℃의 電氣爐와 倒焰式 角堯의 燒成 結果로 比較하였다. 實驗結果 여州粘土의 添加量이 적은 組合이 比較的 높은 白色度를 보였으며 光明丹을 添加한것이 frit를 添加한것보다 맑은 色相과 安定된 熔融狀態를 보여 frit가 發色에 영향을 미치는 것을 알았다. 대체로 融劑의 添加量이 많을 수록 끊는 현상과 pinhole이 많으나 光明丹의 경우는 극히 微微하며 無鉛frit의 경우가 제일 심하게 나타났고 두껍게 適用된 部分이 주로 심한 現象을 보였다. 이 中 가장 좋은 결과를 보인 것을 作品製作에 응용하기 위해 朱赤釉등에 그려 1250℃ 還元炎에서 燒成한 결과 釉藥과 잘 密着하였으므로 熔化化粧土를 이용한 윗그림의 可能性을 나타내었다고 할 수 있다. 필자의 作品에서는 基本素地를 이용하여 물레成形한 것을 900℃로 초벌소성한 후에 銅釉, 주적釉, 黑釉, 乳白釉로 施釉하고 着色劑를 添加시킨 熔化化粧土를 그 위에 應用해 보았으며, 그 결과 유약보다 세밀한 touch의 감각을 나타낼수 있었을 뿐아니라 vitreous coating의 가능성을 기대할 수 있으므로 색소지나 백소지를 이용하여 여러 가지 색상의 용화화장토로 초벌소성된 소지위에 장식한다면 소지의 질감을 그대로 드러내면서 장식되는 다양한 표현을 기대할 수 있겠다.
Fulltext
Show the fulltext
Appears in Collections:
일반대학원 > 조형예술학부 > Theses_Master
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE