자기신장 다층구조사 폴리에스테르 직물과 모직물류의 태평가

Title
자기신장 다층구조사 폴리에스테르 직물과 모직물류의 태평가
Authors
전윤경
Issue Date
2000
Department/Major
대학원 의류직물학과
Publisher
이화여자대학교 대학원
Degree
Master
Abstract
Recently, diverse new worsted-type polyester fabrics, which aim at wool-like characteristics, and hand feel with crispness and stiffness, are being prepared by the technology element comprising false-twist after air-jet entanglement of yarns having different characteristics, for example, different cross-sectional shapes, or different shrinkage properties, even though there are some varied technological details. The technology element employed is the conjugate-texturing technology to construct a sheath-core structure of two polyester filaments of different physical or mechanical characteristics by temporary twisting. The air-jet processing technology is frequently applied. One of the examples is a worsted-type fabric in which a dual yarn structure is comprised of thick filaments of varying linear density as core material, with very fine denier filaments wrapped around the core. This type of fabric is said to have good bulkiness and a hand similar to that of the finest wool fabric. In this study, seven different polyester filament fabrics were compared with similarly structured wool-containing fabrics (50:50, 80:20, 100%). Subjective evaluation of the fabrics were carried out based on the questionnaire with twenty-one adjective pairs including 'smooth-not smooth', 'light-heavy', 'glossy-not glossy', and so on. Objective measurements of the physical/mechanical properties of sample fabrics include KES tensile/shear, surface, compression, beding properties, thermal property(𝐪max), and air-permeability. Polyester fabrics have been known for its glossiness or unpleasant glossiness due to the high refractive index value and the surface characteristics. On top of glossiness measurement using a two-dimensional goniometric glossmeter, a more detailed analysis has been attempted with the help of image analysis technique focusing on micro-facet structure of the fabric specimen. While the gloss measurement gave an simple glossiness characterization, or the 'magnitude of the gloss', the analysis of the fabric images captured under a microscope could explain the details of gloss-characteristics including information about the size distribution of glossy object, which could be interpreted as one measure of the 'quality of the gloss'. There is a good correlation between the 𝐪max readings and the 'warm-cool' feling subjective evaluation result. The values of the ratio of the area of glossy objects to the total image area have some linear relationship with the 'glossy- not glossy' subjective evaluation results. Factor analysis of the subjective evaluation terms has revealed that the twenty abjective pair terms could be grouped into five. The Factor 1 is largely dependent on 'smooth, rough, soft'. The Factor 2 is dependent on 'winkle-prone, glossy, sticky, damp, ...'. The Factor 3 is dependent on 'stringy, stretchy, elastic'. The Factor 4 is dependent on 'hard, stiff, pliable, strong'. The Factor 5 is dependent on 'light, warm, thick,...'. Analysis of variance of the subjective evaluation result has shown that there are significant difference among the samples for adjective pairs.;신합섬 중 뉴소모풍의 부류는 양모의 특징을 나타내며 샤리(SHARI,cripness)와 고시(KOSHI, stiffness)의 태를 지닌 것이다. 뉴소모풍의 원사를 제조할 때에는 물성이 서로 다른 두 필라멘트 장섬유를 가연에 의해 심초구조를 형성하는 복합가공 방법이 필요한데, 심부에 필라멘트 섬도에 변동이 있는 실을 샤용하고 표면에는 섬세한 필라멘트 사를 감는 구조로 제조한 제품은 벌크(bulk)성이 양호하며 고급 양모 직물의 촉감과 유사하여지며, 폴리에스테르의 특징으로서 구김이 적고 플리팅이 용이한 장점도 가지게 된다는 사실이 보고되고 있다. 본 논문에서는 뉴소모풍의 자기 신장 다층구조사 폴리에스테르 직물과 모직직물류의 태를 객관적 평가 방법과 주관적 평가 방법, 광택, 냉온감을 이용해 비교하였다. 직물시료는 폴리에스테르 직물로서는 고분자의 개질을 통해 고수축률을 심사(core)로서 100denier semi-dull filament 원사를 사용하고 표면(effect)에 자기신장형 140denier semi-dull filament 사를 사용하여 독특한 태를 제공하는 뉴-소모풍 직물과 순모직물, 모/폴리에스테르의 혼방(80:20, 50:50)직물을 선정하여 Kawabata 시스템, 광텍도, CCD카메라, 냉온감, 공기투과도 등을 통해 객관적특성을 측정하였고 설문지 조사를 통해 주관적 평가를 하여 직물의 물리적 특성과 실제 소비자가 느끼는 특성을 비교하였다. 객관적 평가 결과에선 자기 신장 다층구조사 폴리에스테르 직물이 인장특성(WT), 굽힘강성(B), 전단강성에서 순모 직물, 모/폴리에스테르 혼방 (80:20, 50:50)직물보다 큰 값이 나왔고, 표면특성(SMD)은 모/폴리에스테르 혼방(50:50)직물이 가장 매끄럽고, 얇은 것으로 나왔으며, 압축특성(WC)은 대체로 자기신장 다층구조사 폴리에스테르 직물이 높은 값을 나타냈다. 각 직물시료에 대한 평가자들으 주관적 평가 결과는 분산분석 결과 21개의 문항 중 2개를 제외한 거의 모든 평가문항에서 시료간의 유의차가 나타내고 있었다. 시료별 주관적 평가결과를 시료별-문항별 평균치로서 비교한 결과, 모/폴리에스테르 혼방(50:50)직물, 순모, 모/폴리에스테르 혼방(80:20)직물 순으로 광택이 있다고 나타났다. 직물표면의 미소평면에서의 광택은 현미경하에서 획득한 화상을 분석함으로서 객관적인 평가가 가능함을 확인하였고, 광택에 대한 주관적인 평가어인 ‘광택이 있다- 광택이 없다’ 문항에 대하여 평가자들이 평가한 결과의 평균값과 미소평면에 대한 광택화상 분석결과 중 광택을 내는 시료의 화상 중의 각 개체를 면적을 합산하여 화상면적에 대한 비율로 계산한 결과사이에는 음의상관이 존재함을 확인할 수 있었다. 일반적인 합성섬유 직물의 결점 중의 하나로 광택이 너무 많은 것을 들 수 있는데 본 연구에 사용한 자기신장 다층구조사 폴리에스테르 직물은 표면의 권회된 섬세한 섬유(TiO₂포함) 및 감량 가공처리에 의해 광택이 상당히 감소한 것을 알 수 있다. 직물 표면의 냉온감의 주관적인 평가결과는 객관적인 측정치인 qmax값과 상당히 좋은 상관 관계를 나타내고 있음을 확인 할 수 있었다.
Fulltext
Show the fulltext
Appears in Collections:
일반대학원 > 의류학과 > Theses_Master
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE