가교 Polystyrene 기체로부터 유도되는 유사-아미드옥심형 Chelate Resin의 합성과 특성화

Abstract

Pseudo-amidoxime type chelate resin was synthesized through the cyanomethylation of gel type crosslinked chloromethylated polystyrene (PCMS) and subsquent amidoxmation of cyanomethylated PCMS (PCMS-CN). As crosslinking agents, Divinylbenzene (DVB) and ethyleneglycol-dimethacrylate (EGD) were added in polymerization of chloromethylstyrene. In cyanomethylation of PCMS, the degree of substitution amounts to 80-90 percent regardless of the kind of crosslinking agent and the degree of crosslinking. Amidoximation accompanied cyclization as side reaction between introduced amidoxime groups was observed. Several models for cyclized reaction were proposed on the basis of chlorine and nitrogen content of amidoximated - PCMS. Pseudo-amidoxime type chelateresin has a low adsorption capacity for metal ions compared with amidoxime type chelate resin derived from crosslinked polyacrylonitrile matrix.;gel형 가교 chloromethyl화 폴리스티렌(PCMS)를 시아노메틸화 시키고 연이어 아미드옥심화 시킴으로써 유사-아미드옥심형 킬레이트 수지를 합성하였다. PCMS의 중합에서는 가교제로서 Divinylbenzene(DVB)와 Etyleneglycol-dimethacrylate(EGD)가 사용되었다. PCMS의 시아노메틸화에서는 PCMS 기체의 가교에 사용된 가교제의 종류와 가교도에 관계없이 치환율이 대략 80~90%에 달하였다. 아미드옥심화 도중 PCMS에 도입전 아미드옥심기들 간의 상호작용에 의해서 고리화 부반응이 수반되었다. 아미드옥심화 PCMS의 질소함량과 염소함량에 의거하여 고리화 반응의 몇 가지 모델을 제시하였다. 가교 Polyacrylonitrile로부터 유도된 아미드옥심형 킬레이트 수지에 비해서 유사-아미드옥심형 킬레이트 수지는 금속이온에 대하여 비교적 낮은 흡착능을 보여주었다.