TRIETHYLENEGLYCOL DIMETHACRYLATE 가교 POLYACRYLONITRILE의 중합과 아미드옥심화 반응에 관한 연구

Abstract

Triethyleneglycol dimethacrylate (TGD_(3)) crosslinked macroreticular type polyacrylonitrile (PAN) was synthesiged. Toluene added as dilution agent lowered the polymerization capacity of acrylonitrile(AN) monomer, especially in low degree of crosslinking maximum surface area of crosslinked PAN was obtained at 60-90% dilution state at all degree of crosslinking. As a result of low degree of crosslinking state caused by TGD_(3) crosslinking agent which has flexible molecular structure and hydrophillic properties, TGD_(3) crosslinked PAN was easily swelled even by toluene. Amidoximation of PAN accompanies the cyclization reaction caused by interaction between CN group and amidoxime group introduced to PAN main chain. Cyclization reaction seemed to be governed by the amount of CN group exist in PAN molecular main chain. Amidoximated PAN chelate resin has an excellent adsorption capacity for Cu^(+2), Cr^(+2), Cd^(+2), Fe^(+2), Pb^(+2). UO_(2)^(+2) ions regardless of pH and concentration of metal ion.;TGD_(3) 가교 macroreticular형(그물형) polyacylonitrile(PAN)이 제조되었다. 중합시 희석제로 첨가된 toluene은 acrylonitrile (AN)의 중합능을 저하시키는데 낮은 가교도 일수록 그 효과가 크게 나타난다. 가교 PAN의 최대표면적은 가교도에 관계없이 희석을 60 ~ 90 %에서 얻어졌다. 유연한 분자구조와 친수성을 지니는 TGD_(3)가교제는 가교 PAN 내부에 느슨한 가교상태를 부여하기 때문에 비용매인 toluene에 대해서도 PAN은 쉽게 팽윤된다. PAN의 아미드옥심과 도중 PAN주쇄위에 존재하는 CN기와 아미드옥심간의 상호작용으로 인하여 부반응인 고리화 반응이 수반된다. 고리화 부반응은 PAN 주쇄위에 존재하고 CN기 함량에 의해서 지배된다. 아미드옥심과 PAN은 pH와 금속이온의 농도에 영향을 받지않고 Cu^(+2), Cr^(+2), Fe^(+2), Pb^(+2), Uo_(2)^(+2) 등에 대하여 뛰어난 흡착능을 지닌다.