유지놀 함유 임시충전재의 사용이 복합레진의 미세누출에 미치는 영향

Title
유지놀 함유 임시충전재의 사용이 복합레진의 미세누출에 미치는 영향
Other Titles
Effect of eugenol containing temporary material on the microleakage of composite resin restorations
Authors
손선나
Issue Date
2009
Department/Major
임상치의학대학원 임상치의학과임상소아치과학전공
Publisher
이화여자대학교 임상치의학대학원
Degree
Master
Advisors
정영정
Abstract
The purpose of this study was to evaluate and compare the effect of eugenol containing temporary material on the microleakage of composite resin restorations. Access cavities were prepared in forty four sound human permanent molars. The prepared teeth were randomly divided into four groups. The teeth of group 1 and 3 were filled with IRM(eugenol containing temporary filling material), and the teeth of group 2 and 4 were filled with Cavit(eugenol free temporary filling material). The temporary restorations were removed mechanically with an ultrasonic scaler after 1 hour(group 1 and 2) and 7 days(group 3 and 4). The specimens were restored with composite resin(Filtek™ Z350) after application of self etching primer adhesive(Clearfil SE Bond). After thermocycling, the specimens were stained and immersed in 1% methylene blue solution for dye penetration testing. The teeth was sectioned buccolingually along the long axis, of the teeth and linear depth of dye penetration was evaluated with stereoscope. The results were analysed using Fisher's exact test. The result of this study were as follows. 1. Microleakages of groups with eugenol containing temporary material(group 1 and 3) were not statistically different from those of groups with eugenol-free temporary material(group 2 and 4). 2. Microleakages were not statistically different between group(group 3) with in which composite resin was filled 7 days after eugenol containing temporary material was filled was not statistically different from that of group(group 1) in which composite resin was filled 1 hour after eugenol containing temporary material was filled. 3. SEM images of resin-tooth interfaces showed interfacial gaps between composite resin and enamel in all groups(group 1~ 4). According to the result of this study, microleakge was more affected by the procedure of composite resin filling than by the presence of eugenol or period of eugenol diffusion. Therefore, thorough removal of temporary filling materials and meticulous filling of composite resin should be done.;본 연구의 목적은 유지놀 함유 임시충전재의 충전 후 복합레진 수복시 미세누출에 미치는 영향을 평가하기 위함이다. 우식병소와 수복물 및 미세균열이 없는 발치된 상하악 대구치 44개를 실험치아로 선별하여 1급 와동을 형성하였으며, 무작위로 10개씩 4개의 군으로 나누어 실험하였다. 1군과 3군은 유지놀 함유 임시충전재군으로IRM(Dentsply, Milford, USA)을 충전하였으며, 2군과 4군은 유지놀 비함유 임시충전재군으로 Cavit(ESPE, Seefeld, Germany)를 충전하였다. 각 군의 임시충전재는 초음파 스케일러를 이용하여 1시간 후(1군과 2군)와 7일후(3군과 4군)에 기계적으로 제거하였다. 각 군의 치아는 광중합 복합레진 FiltekZ350(3M, MN, U.S.A)을 사용하였고, 접착제는 자가 산부식 프라이머 접착제인 Clearfill SE Bond (Kurary, Okayama, Japan)을 사용하였다. 열순환 후 각 치아는 색 침투를 위하여 1% 메틸렌 블루 용액에 침전시켰다. 치아 장축 협설 방향으로 절단하여 시편을 제작한 후 현미경을 이용하여 색침투 깊이를 측정하였다. 통계분석은 피셔의 정확검정을 시행하였다. 그 결과는 다음과 같다. 1. eugenol 함유 임시 충전재군과 eugenol 비함유 임시충전재군 간의 차이는 유의하지 않았다(p>0.05). 2. 유지놀 함유 임시충전재의 충전 기간에 따른 1군(1시간후)과 3군 (7일후)의 두 군 간에 유의한 차이를 보이지 않았다. 3. 주사전자현미경으로 접착단면을 관찰한 결과 복합레진과 법랑질의 접착 계면에 간극이 다소 관찰되었으나, 유지놀 함유군(1,3)과 유지놀 비함유군(2,4)간의 차이점을 발견할 수 없었다. 위의 결과를 통해 복합레진의 미세누출은 임시 충전재 내의 유지놀 함유 여부의 직접적인 영향보다는 충전 시의 절차에 따라 영향을 받는 것으로 보이므로, 충전 과정에 더욱 신중을 기해야 할 것으로 생각된다.
Fulltext
Show the fulltext
Appears in Collections:
임상치의학대학원 > 임상소아치과학전공 > Theses_Master
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE