Crawling釉에 관한 연구

Title
Crawling釉에 관한 연구
Other Titles
(A) Study on Crawling Glazes
Authors
이미경
Issue Date
1992
Department/Major
산업미술대학원 산업미술학과요업디자인전공
Keywords
Crawling유발색제유약자기유약유색변화도예자기
Publisher
이화여자대학교 산업대학원
Degree
Master
Abstract
Modern times is rushing toward the unpredicatable unknown world by the endless human infinite desire. For example, the human yearing about the beautiful mineral which exists in the natural world unusally became the deep attachment to try to change the earth and rocks into jade. Glaze is the mixture of many kinds of materials made naturally and artificially, and the glaze manyfacture about this has already been continued for several centuries, and it may be most natural to make and develop another glaze. It can be seen that crawling glaze was frequently discovered from the Faience ceramic of Egypt and the tea bowl of Koryo and it was frequently applied to many tea bowls. As for the crawling phenomenon, if is that the glaze of utensil surface was rolled and united together, and it is what forms the small beads similar to waterdrop on the oily surface or wax surface. Then, the surface tension of glaze is the representative cause. This glaze which was discovered from the foot part of the tea bowl of Koryo formerly was indicated as the big defect of glaze. Thus, it is considered that, perhaps, the potters have groped for only the method to try to remove this mainly. So, the purpose of this study is to study the definition and generation factor of crawling by collections and analyzing the study data about crawling up to recent times since 1950's, and to discover the production range to be able to obtain the crawling by changing the production of glaze on the basis of the mixing of general porcelain glaze and to discover the possibility of effective decoration through the diverse crawling glaze based on mutually correspondent material union and the change of coloring thickness. For the glaze experiment, the external appearance state of crawling was observed, by calcining the reduction fire in 1250℃, with the change of rate of adding the oxides, MgO, MgCO_(3), CaO and ZnO which influence the crawling and of which the surface tension is big to 30 kinds of glazes produced by selecting by selecting the calcareous galze(0.3 Na_(2)O.·0.7 CaO.·0.5 Al_(2)O_(3).·4.0 SiO_(3)) as the base glaze, first of all and then changing only the equivalent of Al_(2)O_(3) and SiO_(2) without changing the basic components. And, in the Sager formula of the basic glaze about material, that is, feldspathic glaze, calcareous glaze, lime, magnesia glaze, and barium glaze, 15 kinds of glazes produced by fixing the equivalent of Al_(2)O_(3) and SiO_(2) higher than the calcareous glaze which is basic galze was observed by calcining in the same temperature respectively Again, in Sager formula of calcareous glaze which was basic glaze in the above experiment of 2 component group, the external appearance form and the existense or non-existence of crawling etc. were compared and examined from the glaze produced by fixing Na_(2)O to 0 3 mole and repiacing 0.7 mole component of CaO with the each material (oxide, hydroxide) of CaO, MgO and Ca(OH)_(2). This researcher tried to observe the change of diverse glaze color and the effect of crawling, by selecting the glaze of which the crawling phenomenon is in the best state from the experiment result of 2 component group and by adding color former. As the color formers, the metal oxides of CuO, CoO, Cr_(2)O_(3), Fe_(2)O_(3), MnO_(2), NiO, TiO_(2), V_(2)O_(5) were used. And, the reducing flame calcination was made in 1250℃ by applying them to celadon porcelain and white porcelain respectively. And, as for the experiment of paint addition, oxidizing flame calcination was made in the same calcination temperature. In this experiment result, it can be seen that the external appearance state of glaze is changed largely by the equivalent change of Al_(2)O_(3) and SiO_(2). Then, it could be seen that the crawling phenomen is remarkable, according as the equivalent of SiO_(2) getting higher than that of Al_(2)O_(3). And, it could be seen that the crawling phenomenon appears remarkably, according as the equivalent of MgO, CaO and MgcO_(3) of which the surface tension is big is large. On the other hand, it could be seen that the exfoliation phenomenon of glaze is appears because fusion is not made, according as the equivalent of Al_(2)O_(3) is high. And, it could be seen that the size of crawl may be controiled according to the glazing thickness Then, it could be seen that the crawling is formed largely, according as the glazing thickness is thick. As for the calcination, the color change and the state change of crawling based on the addition of color former could be seen, with the reducing flame calcination. Through above experiment, it could be discovered that crawling glaze may give another new decorative possibility, and it is deemed that the application of variable crawling phenomenon may satisfy the modern ceramic art with diverse and attractive effect.;현대는 끊일 줄 모르는 인간의 무한한 욕망에 의 하여 예측할 수 없는 미지의 세계로 줄달음치고 있다. 예컨대, 자연계에 드물게 존재하는 아름다운 광물에 대한 동경은, 이윽고 土石을 玉으로 바꾸려는 집념이 되었다. 釉藥은 여러 증류의 자연적 또는 인공적으로 만들어진 原料의 혼합이며, 이에 대한 釉藥製造는 이미 몇 세기 동안 계속되어 왔으며, 또 다른 釉藥을 만들고 발전시키는 일은 지극히 당연한 일일 것이다. Crawling釉는 고대 Egypt의 Faience Ceramic과 高麗茶碗에서 흔하게 발견되었고, 日本의 여러 茶碗에 많이 응용되어진 것을 볼 수 있다. Crawling현상은 기물 표면의 釉藥이 말려 뭉쳐진 것으로 심지어 기름기 흐르는 표면 혹은 Wax표면 위의 물방울과 흡사한 작은 구슬(beads)들을 형성하는 것으로 釉藥의 표면장력(surface tension)이 그 대표적인 원인이다. 일찌기 高麗 茶碗 (tea bowl)의 굽부분에서 발견되었던 이 釉藥은 결점으로 지적되어 이를 제거하려는 방법만을 주로 모색해 왔을 것으로 생각된다. 그러므로 本 硏究에서는 Crawling에 관한 1950년대부터 최근까지의 연구자료를 수집 분석하여 Crawling의 정의 및 발생요인을 고찰하고 일반 磁器釉藥 調合을 토대로 釉藥의 조성을 변화시켜서 Crawling을 얻을 수 있는 원료의 결합과 착색두께의 변화에 따른 다양한 Crawling釉藥을 통하여 효과 높은 장식의 가능성을 발견하는데 目的을 두었다. 本 硏究의 Crawling釉藥實驗을 위하여 釉의 유동성을 방해하고, 높은 장력(tension)을 가진 CaO성분으로 조성된 용융온도범위가 넓은 石灰釉(0.3 Na_(2)O.·0.7 CaO.·0.5 Al_(2)O_(3).·4.0 SiO_(2)) 를 基本釉로 선정하였다. 우선 여기에 염기성 성분들은 변화시키지 않고 Al_(2)O_(3) 과 SiO_(2)의 당량(equiralent weight)만을 변화시켜 조성된 30종류의 釉에 Crawling에 영향을 주는 표면장력이 큰 산화물들인 MgO, HgCO_(3), CaO, ZnO의 첨가比변화로, 1.3 ㎥ 倒焰式 gas角가마에서 1250℃로 환원소성 하여 Crawling의 외관상태를 관찰하였다. 그리고 熔劑原料증류에 의한 磁器基礎釉, 즉 長石釉, 石灰釉, 石灰-마그네샤釉, 마그네샤釉, 바륨釉의 Seger式에서 Al_(2)P_(3)의 당량을 1mole에서 1.2mole까지 0.1mole간격으로, SiO_(2)의 당량을 2mole에서 6mole까지 1mole간격으로 변화시켜 조성한 釉들을 동일한 가마에서 1250℃로 환원소성 하여 관찰하였다. 다시 本실험의 石灰釉 Seger式에서 염기성 성분 중 Na_(2)O는 0.3mole로 고정시키고, 0.7mole의 CaO를 CaO, MgO, Ca(OH)_(2)의 각각의 원료로(산화물, 수산화물) 치환시켜 조성된 釉에서 外觀性狀, Crawling의 有無 등을 비교 검토하였다. Al_(2)O_(3) - SiO_(2) 二成分系의 實驗結果 중 Crawling 현상이 가장 양호한 상태인 실험G의 27번釉(0.3 Na_(2)O·0.7 MgO·0.9 Al_(2)O_(3)·3SiO_(2))를 선정하여 發色濟를 첨가해서 다양한 釉色변화와 Crawling의 효과도 관찰하고자 하였다. 발색제로는 CuO, CoO, Cr_(2)O_(3), Fe_(2)O_(3), MnO_(2), NiO, TiO_(2), V_(2)O_(5), 의 금속 산화물을 사용하여 청자소지와 백자소지에 각각 적용시켜 역시 1.3㎥ 倒焰式 gas角가마를 사용하여 1250℃로 환원소성하고 안료첨가실험도 동일한 소성온도에서 산화소성 하였다. 이러한 실험결과에서 Al_(2)O_(3) 와 SiO_(2) 의 당량 변화에 의해 釉의 외관상태가 크게 변화하는 것을 볼 수 있는데 특히 Al_(2)O_(3)의 당량보다 SiO_(2)의 당량이 높아질수록 Crawling 현상이 현저함을 알 수 있었다. 또 표면장력이 큰 MgO, CaO, MgCO_(3) 등의 당량이 클수록 Crawling 현상이 두드러지게 나타남을 알 수 있었으며, 특히 Al_(2)O_(3)의 당량이 높을수록 不熔融되어 釉의 剝落(peeling off) 현상이 나타났다. 그리고 釉의 시유두께에 따라 Crawl의 크기를 조절할 수 있음을 알았는데, 시유두께가 두꺼울수록 Crawling이 크게 형성되는 것을 알 수 있었다. 일반적으로 陶藝의 磁器에 쓰이는 生釉들은 1200~1300℃의 범위에서 主로 환원소성하는 경우가 많다. 그러므로 本 硏究에서는 釉의 발색변화보다는 Crawling현상을 관찰하고자 하는 것으로 1250℃의 소성온도와 환원염을 택하여 실험하였다. 위의 실험을 통해서 Crawling釉藥이 또 하나의 새로운 장식적 가능성을 부여할 수 있음을 발견하게 되었으며 변화있는 Crawling현상의 응용은 다양하고 매력적인 효과로서 現代陶磁藝術에 부응하리라고 생각된다.
Fulltext
Show the fulltext
Appears in Collections:
디자인대학원 > 도자디자인전공 > Theses_Master
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE